GMC Yukon 2000–2006

GMC YukonModel years 2000–2006

Change vehicle →
Clear the search
2 conditions added

Common on this vehicle:Vibration or shudderTyre failure (blowout, tread separation)NoiseWarning lightCorrosion or rustLeakAir conditioning or heaterABS activates (at low speed and the like)

Record by record

11 records state a cause or a remedy. Each record is shown as short labels in the order fault → finding the cause → correction. Press a label to narrow to the records that state it.

Symptom

Component named as the cause

Work done

How it is said to have ended

  • says it did not fix it1
  • result not stated2

A ribbon is as wide as the records that state both of its ends (only the commonest are drawn). A record that names several symptoms or components runs through each. Orange is records that say the fault came back or was not fixed. Results come from owners’ reports only; one that does not say is “result not stated”. None of this is a likelihood of a cause or a rate at which work succeeds.

Read the records one by one (8)

Known issuesUnwanted ABS activation at low speed (front wheel speed sensor mounting corrosion)1

  1. Owner complaint2002 GMC YUKON ・ 2010-03-23

    ABS activation during slow stops, increased stopping distance

    1. 1Fault

    2. 2Finding the cause

    3. 3Correction

    Read the sentences of the record
    Fault
    ABS ACTIVATES DURING SLOW STOPS, INCREASES STOPPING DISTANCE.
    Cause
    I BELIEVE PROBLEM IS CORROSION IN FRONT WHEEL HUBS ON TONE RING.
    Remedy
    DEALER REPLACED BOTH FRONT SPEED SENSORS AND PROBLEM PERSISTS.

Known issuesBrake pipe (brake line) corrosion and rupture1

  1. Owner complaint2000 GMC YUKON ・ 2014-01-23

    Brake failure and ABS activation while driving, brake line corroded

    1. 1Fault

    2. 2Finding the cause

    3. 3CorrectionNot repaired

    Read the sentences of the record
    Fault
    THE CONTACT STATED THAT WHILE DRIVING APPROXIMATELY 5 MPH (= 8.05 km/h), THE BRAKES FAILED TO ENGAGE WHEN DEPRESSED AND THE BRAKE PEDAL ABNORMALLY TRAVELED TO THE FLOOR BOARD. (1 more)
    Remedy
    THE VEHICLE WAS NOT REPAIRED. (1 more)
    Inspection
    THE VEHICLE WAS TAKEN TO A DEALER WHERE IT WAS DISCOVERED THAT THE BRAKE LINE WAS CORRODED.

EQUIPMENT3

  1. Manufacturer communication2000–2006 GMC YUKON DENALI ・ 2021-04-26

    Aluminum Wheel Refinishing Service Bulletin

    1. 1Fault

    2. 2Finding the cause

      Not stated

    3. 3Correction

      Refinishing Aluminum Wheels This bulletin updates General Motor's position on refinishing aluminum wheels. GM does not endorse any repairs that involve welding, bending, straightening o re-machining. Only cosmetic refinishing of the wheel's coatings, using recommended procedures, is allowed. Evaluating Damage In evaluating damage, it is the GM Dealer's responsibility to inspect the wheel for corrosion, scrapes, gouges, etc. The Dealer must insure that such damage is not deeper than what can be sanded or polished off. The wheel must be inspected for cracks. If cracks are found, discard the wheel. Any wheels with bent rim flanges must not be repaired or refinished. Wheels that have been refinished by an outside company must be returned to the same vehicle. The Dealer must record the wheel ID stamp or the cast date on the wheel in order to assure this requirement. Refer to Refinisher's Responsibility — Outside Company later in this bulletin.

    Read the sentences of the record
    Remedy
    Refinishing Aluminum Wheels This bulletin updates General Motor's position on refinishing aluminum wheels. GM does not endorse any repairs that involve welding, bending, straightening o re-machining. Only cosmetic refinishing of the wheel's coatings, using recommended procedures, is allowed. Evaluating Damage In evaluating damage, it is the GM Dealer's responsibility to inspect the wheel for corrosion, scrapes, gouges, etc. The Dealer must insure that such damage is not deeper than what can be sanded or polished off. The wheel must be inspected for cracks. If cracks are found, discard the wheel. Any wheels with bent rim flanges must not be repaired or refinished. Wheels that have been refinished by an outside company must be returned to the same vehicle. The Dealer must record the wheel ID stamp or the cast date on the wheel in order to assure this requirement. Refer to Refinisher's Responsibility — Outside Company later in this bulletin.

  2. Manufacturer communication2000–2006 GMC YUKON DENALI ・ 2021-04-26

    Aluminum Wheel Refinishing Guidelines

    1. 1Fault

    2. 2Finding the cause

      Not stated

    3. 3Correction

      Refinishing Aluminum Wheels This bulletin updates General Motor's position on refinishing aluminum wheels. GM does not endorse any repairs that involve welding, bending, straightening o re-machining. Only cosmetic refinishing of the wheel's coatings, using recommended procedures, is allowed. Evaluating Damage In evaluating damage, it is the GM Dealer's responsibility to inspect the wheel for corrosion, scrapes, gouges, etc. The Dealer must insure that such damage is not deeper than what can be sanded or polished off. The wheel must be inspected for cracks. If cracks are found, discard the wheel. Any wheels with bent rim flanges must not be repaired or refinished. Wheels that have been refinished by an outside company must be returned to the same vehicle. The Dealer must record the wheel ID stamp or the cast date on the wheel in order to assure this requirement. Refer to Refinisher's Responsibility — Outside Company later in this bulletin.

    Read the sentences of the record
    Remedy
    Refinishing Aluminum Wheels This bulletin updates General Motor's position on refinishing aluminum wheels. GM does not endorse any repairs that involve welding, bending, straightening o re-machining. Only cosmetic refinishing of the wheel's coatings, using recommended procedures, is allowed. Evaluating Damage In evaluating damage, it is the GM Dealer's responsibility to inspect the wheel for corrosion, scrapes, gouges, etc. The Dealer must insure that such damage is not deeper than what can be sanded or polished off. The wheel must be inspected for cracks. If cracks are found, discard the wheel. Any wheels with bent rim flanges must not be repaired or refinished. Wheels that have been refinished by an outside company must be returned to the same vehicle. The Dealer must record the wheel ID stamp or the cast date on the wheel in order to assure this requirement. Refer to Refinisher's Responsibility — Outside Company later in this bulletin.

  3. Manufacturer communication2005–2006 GMC YUKON DENALI ・ 2019-12-16(1 earlier editions of this document folded here)

    Aluminum wheel bead seat cleaning and resurfacing procedure

    1. 1Fault

      • A tire slowly loses air pressure over a period of days or weeks.

    2. 2Finding the cause

      Possible causes

      • Abrasive elements may intrude between the tire and wheel at the bead seat, and the relative motion between tire and wheel lets the particles wear the wheel and tire materials.

      Steps to confirm (in the document’s order)

      1. The corrosion may be on the inboard or outboard bead seating surface and is not visible until the tire is dismounted from the wheel.
      2. After a water dunk tank leak test, if the source of the leak is around the bead seat of the wheel, dismount the tire to examine the bead seat.
      3. Bead seat corrosion looks like blistering of the wheel finish, giving a rough or uneven surface on which the tire has difficulty keeping a proper seal.
      4. For vehicles with 32,186 km (20,000 mi) or less, the total combined linear area of repairable corrosion is 100 mm (4 in) or less; beyond that the wheel should be replaced.
      5. For vehicles that have exceeded 32,186 km (20,000 mi), the total combined linear area of repairable corrosion is 200 mm (8 in) or less.

    3. 3Correction

      Repair

      1. Use a clean-up (fine cut) sanding disc or biscuit to remove the corrosion and any flaking paint, back to material that is stable and firmly bonded to the wheel.
      2. Once the corrosion is eliminated, coat the repaired area with a commercially available tire sealant such as Patch Brand Bead Sealant or equivalent.

      Parts

      • Part number 16118, Patch Bead Sealer (1 Quart (= 0.946 L)).

      Caution

      • Do not replace a wheel for slow air loss unless the wheel has been evaluated and/or repair has been tried with this procedure.
    Read the sentences of the record

    From the manufacturer’s document

    • Applies to：Applies to 2005-2020 GM passenger cars and light duty trucks.
    • Condition：A tire slowly loses air pressure over a period of days or weeks.
    • Cause：Abrasive elements may intrude between the tire and wheel at the bead seat, and the relative motion between tire and wheel lets the particles wear the wheel and tire materials.
    • Confirm：The corrosion may be on the inboard or outboard bead seating surface and is not visible until the tire is dismounted from the wheel.
    • Caution：Do not replace a wheel for slow air loss unless the wheel has been evaluated and/or repair has been tried with this procedure.
    • Confirm：After a water dunk tank leak test, if the source of the leak is around the bead seat of the wheel, dismount the tire to examine the bead seat.
    • Confirm：Bead seat corrosion looks like blistering of the wheel finish, giving a rough or uneven surface on which the tire has difficulty keeping a proper seal.
    • Confirm：For vehicles with 32,186 km (20,000 mi) or less, the total combined linear area of repairable corrosion is 100 mm (4 in) or less; beyond that the wheel should be replaced.
    • Confirm：For vehicles that have exceeded 32,186 km (20,000 mi), the total combined linear area of repairable corrosion is 200 mm (8 in) or less.
    • Repair：Use a clean-up (fine cut) sanding disc or biscuit to remove the corrosion and any flaking paint, back to material that is stable and firmly bonded to the wheel.
    • Repair：Once the corrosion is eliminated, coat the repaired area with a commercially available tire sealant such as Patch Brand Bead Sealant or equivalent.
    • Parts：Part number 16118, Patch Bead Sealer (1 Quart (= 0.946 L)).

    Open the manufacturer’s document (PDF) ↗ The points above were read from this document.

    Remedy
    This technical bulletin provides a procedure on how to clean and resurface aluminum wheel bead seats for vehicles that have the condition of Tire Slowly Goes Flat, Tire Air Loss, Low Tire Pressure Warning Light Illuminated, Aluminum Wheel Bead Seat Corrosion.

SERVICE BRAKES, HYDRAULIC1

  1. Owner complaint2002 GMC YUKON ・ 2005-11-30

    Front wheel assembly replacement on 2002 GMC Yukon

    1. 1Fault

    2. 2Finding the cause

    3. 3Correction

    Read the sentences of the record
    Remedy
    2002 GMC YUKON FRONT WHEEL ASSEMBLY HAD TO BE REPLACED.

SUSPENSION1

  1. Owner complaint2002 GMC YUKON ・ 2012-07-10

    Banging noise from rear while driving

    1. 1Fault

    2. 2Finding the cause

    3. 3Correction

      Not stated

    Read the sentences of the record
    Fault
    THE CONTACT STATED WHILE DRIVING 25 MPH (= 40.2 km/h) THERE WAS A BANGING NOISE COMING FROM THE REAR OF THE VEHICLE.

WHEELS1

  1. Manufacturer communication2005–2006 GMC YUKON DENALI ・ 2018-06-04(2 earlier editions of this document folded here)

    Chromed Aluminum Wheels—Chemical Staining and Corrosion

    1. 1Fault

    2. 2Finding the cause

      Possible causes

      • Chemical staining mostly results from acid based cleaners; the stains are frequently milky, black or greenish.
      • A second type of staining comes from road chemicals such as calcium chloride used for dust control on unpaved roads; it looks like small pitting.
      • A third type comes from prolonged exposure to brake dust, which penetrates the chrome.

    3. 3Correction

      Repair

      1. After cleaning, wax the wheel with ACDelco Cleaner Wax, P/N 88865218 (in Canada, 2675208), to protect it from brake dust.
      2. For milky stains from acidic cleaners, apply 3M Chrome and Metal Polish #39527 with a clean terry cloth towel; the staining diminishes as it is applied.

      Part numbers printed in the document

      The numbers are as the document prints them. The name and the replacing number are what the pages of GMPartsGiant, a reseller of genuine parts and not GM, state. Aftermarket equivalents are not checked here (the links only search by number). Confirm the fit for the vehicle (VIN) before ordering.

      Caution

      • Do not use cleaning solutions containing hydrofluoric, oxalic and most other acids on chrome wheels (or any wheels).
      • Any wheel cleaner must be thoroughly rinsed off the wheel with clean, clear water.
      • The wheels must be cleaned before the polish is applied, to avoid scratching the wheel surface.
      • The polish reduces the thickness of the chrome plating and, used incorrectly or excessively, may remove it altogether.
      • On wheels spotted by road chemicals the procedure may improve the condition marginally but will not restore the finish or remove the pitting.
    Read the sentences of the record

    From the manufacturer’s document

    • Applies to：2015 and prior GM passenger cars and trucks.
    • Cause：Chemical staining mostly results from acid based cleaners; the stains are frequently milky, black or greenish.
    • Caution：Do not use cleaning solutions containing hydrofluoric, oxalic and most other acids on chrome wheels (or any wheels).
    • Caution：Any wheel cleaner must be thoroughly rinsed off the wheel with clean, clear water.
    • Cause：A second type of staining comes from road chemicals such as calcium chloride used for dust control on unpaved roads; it looks like small pitting.
    • Cause：A third type comes from prolonged exposure to brake dust, which penetrates the chrome.
    • Repair：After cleaning, wax the wheel with ACDelco Cleaner Wax, P/N 88865218 (in Canada, 2675208), to protect it from brake dust.
    • Repair：For milky stains from acidic cleaners, apply 3M Chrome and Metal Polish #39527 with a clean terry cloth towel; the staining diminishes as it is applied.
    • Caution：The wheels must be cleaned before the polish is applied, to avoid scratching the wheel surface.
    • Caution：The polish reduces the thickness of the chrome plating and, used incorrectly or excessively, may remove it altogether.
    • Caution：On wheels spotted by road chemicals the procedure may improve the condition marginally but will not restore the finish or remove the pitting.

    Open the manufacturer’s document (PDF) ↗ The points above were read from this document.

    Remedy
    This informational bulletin provides information on chemical staining, pitting, corrosion and/or spotted appearance of chromed aluminum wheels, along with warranty information regarding these conditions.